台式雙麵電池PID測試儀用於單麵及雙麵電池，HIT、Topcon、PERC/PERC+太陽能電池、晶體矽太陽能電池、微型模塊等的質量控製Freiberg公司與德國FraunhoferCSP公司合作開發了一種可作為商業應用的台式太陽能電池和微型模塊的電勢誘導退控製的測量解決方案

標準試驗條件:        

● 電壓:upto1.5kV

● 溫度:85°C

● 測試時間:4hours(typical)

● 幹燥條件下，不需要水

類型                          受壓                                                     恢複
PID-s正麵                85°C，+1.5 kV                             85°C，-1.5 kV

PID-p背麵             85°C，+1.5 kV，無照明 85°C，        暗儲(chu) 存或光照

PID-c背麵                   85°C，+1.5 kV， 照明                    不可恢複

層壓      150°C，20min

樣品尺寸   210×210mm

適用於(yu) A   PERC,AL-BSF,IBC,PERC+,雙麵PERC,p型和n型電池 功率要求 110/230 V AC, 50/60 Hz

資質認證   根據ISO9001準則製造，符合CE標準

參考文獻： cells  (1)K. Sporleder, V. Naumann, J. Bauer, S. Richter, A. Hähnel, S. Großer, M. Turek, C. Hagendorf, Local corrosion of silicon as root cause for potential induced  degradation at the rear side of bifacial PERC solar cells. physica status solidi (RRL)–Rapid Research Letters. 2019, doi 10.1002/pssr.201900163

(2)V. Naumann, K. Ilse, M. Pander, J. Tröndle, K. Sporleder, C. Hagendorf, Influence of soiling and moisture ingress on long term PID susceptibility of photovoltaic

modules, AIP Conference Proceedings 2147, 090005 (2019).

(3)K. Sporleder, V. Naumann, J. Bauer, S. Richter, A. Hähnel, S. Großer, M. Turek, C. Hagendorf, Root cause analysis on corrosive potential-induced degradation effects  at the rear side of bifacial silicon PERC solar cells, Solar Energy Materials and Solar Cells 201, 110062 (2019).

(4)K. Sporleder, V. Naumann, J. Bauer, S. Richter, A. Hähnel, S. Großer, M. Turek, C. Hagendorf, Microstructural Analysis of Local Silicon Corrosion of Bifacial Solar Cells

as Root Cause of Potential‐Induced Degradation at the Rear Side, Phys. Status Solidi A (2019), doi:10.1002/pssa.201900334.

(5)K. Sporleder, J. Bauer, S. Großer, S. Richter, A. Hähnel, M. Turek, V. Naumann, K. Ilse, C. Hagendorf, Potential-Induced Degradation of Bifacial PERC Solar Cells Under  Illumination, IEEE Journal of Photovoltaics 9 (6) 1522-1525, 2019.

(6)K. Sporleder, M. Turek, N. Schüler, V. Naumann, D. Hevisov, C. Pöblau, S. Großer, H. Schulte-Huxel, J. Bauer, C. Hagendorf, Quick test for reversible and irreversible  PID of bifacial PERC solar cells, Solar Energy Materials and Solar Cells 219, 110755, 2021.

(7)K. Sporleder, V. Naumann, J. Bauer, D. Hevisov, M. Turek, and C. Hagendorf, Time-resolved Investigation of Transient Field Effect Passivation States during Potential  Induced Degradation and Recovery of Bifacial Silicon Solar Cells , Solar RRL, 2021, accepted.